EN 10277:2018 standard

W.NR.: 1.1181

Non-alloy special steel

heat analysis according to the EN ISO 683-1:2018 standard

C % Si % Mn % P % S % Cr % Ni % Mo % Cu % Cr+Mo+Ni %
From 0,32 0,10 0,50
To 0,39 0,40 0,80 0,030 0,035 0,40 0,40 0,10 0,30 0,63

according to the EN 10277:2018 standard

Thickness mm Rolled + peeled rolled
( +SH )
Cold drawn
( +C )
hardness HB Rm (MPa) Rp0,2  minimum Rm (MPa) A5 %
(MPa) minimum
≥5≤10 510 da 650 a 1000 6
>10≤16 420 da 600 a 950 7
>16≤40 da 156 a 204 da 520 a 700 320 da 580 a 880 8
>40≤63 da 156 a 204 da 520 a 700 300 da 550 a 840 9
>63≤100 da 156 a 204 da 520 a 700 270 da 520 a 800 9

* Delivery condition: as rolled.

Weldability:
It can be welded quite well without any precautions.

Hardenability:
Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned,  it hardens only till a certain depth, inversely proportional to diameter, like all non-alloy steels with medium-high carbon content.

Notes:

CORRESPONDENCE WITH OTHER STANDARDS (purely as an indication):

 

UNI 7845 DIN 17200 AISI-SAE AFNOR 35-552
 C35  CK35 1035  XC38H1