Cold drawn EN 10277:2018 standard
W.NR.: 1.0760
High machinability steel for direct hardening
heat analysis according to the EN ISO 683-4:2018 standard
| C % | Si % | Mn % | P % | S % | |
| From | 0,35 | – | 1,20 | – | 0,24 |
| To | 0,40 | 0,40 | 1,50 | 0,06 | 0,33 |
according to the EN 10277:2018 standard
| Thickness mm |
Rolled + peeled rolled ( +SH ) |
Cold drawn ( C+ ) |
|||
| hardness HB max | Rm (MPa) | Rp0,2 minimum | Rm (MPa) | A5 % | |
| (MPa) | minimum | ||||
| ≥5≤10 | 550 | da 700 a 960 | 6 | ||
| >10≤16 | 500 | da 660 a 930 | 6 | ||
| >16≤40 | 213 | da 560 a 730 | 420 | da 610 a 900 | 7 |
| >40≤63 | 213 | da 560 a 730 | 400 | da 600 a 840 | 7 |
| >63≤100 | 204 | da 550 a 700 | 350 | da 580 a 820 | 8 |
* Delivery condition: as rolled.
Machinability:
This steel grade generally shows a quite good machinability on machine tools; machinability decreases with the increase of carbon, silicon and manganese content.
Weldability:
Due to the high sulphur and phophorus content free-cutting steels for direct hardening are not recommended for welding.
Notes:
CORRESPONDENCE WITH OTHER STANDARDS (purely as an indication):
| UNI 4838 | AFNOR 35-562 | EN 10087 | EN 10277-3:08 |
| / | / | 38SMn28 | 38SMn28 |