EN 10083-2:98 standard

W.NR.: 1.0402

Non-alloy high grade steel

heat analysis according to the EN 10083-2: 98 standard

  C % Si % Mn % P % S % Cr % Ni % Mo % Cr+Mo+Ni %
From 0,17 0,40
To 0,24 0,40 0,70 0,045 0,045 0,40 0,40 0,10 0,63

according to the UNI 10233-3 standard

Thickness
mm
Cold drawn
( +C )
Rp0,2  minimum Rm minimum A5 %
(MPa) (MPa) minimum
≤5 450,00 570,00 5,00
>5≤10 400,00 520,00 6,00
>10≤16 340,00 520,00 7,00
>16≤25 310,00 520,00 8,00
>25≤40 265,00 460,00 9,00
>40≤100 205,00 380,00 11,00
>100 205,00 380,00 11,00

* Delivery condition: as rolled.

Semi-hard, tough carbon-steel, easily machinable by cold-strain.

Weldability:
Easily weldable.

Hardenability:
Extremely low hardenability, used above all for pieces of small section and when deformations due to water-quenching are allowed.

Notes:

CORRESPONDENCE WITH OTHER STANDARDS (purely as an indication):

 

DIN 17200
 C22

C22.pdf